Login/Join to ParticipatePosted:Im planning on making a new staff soon that will be far superior to my current one which is made from Aluminium (I think)
I was planning on sticking with Al and have just learnt that putting a wooden core in your staff stops it from bending...........which is exactly why Im making a new one!!!
Does anyone have any suggestions as to what would be the best kind of wood to use for a core? It needs to have some flex but be quite strong.
Also, any info on fixing wicks would be appreciated, Im using double wicks.
Kuro
[ 21 August 2002, 20:36: Message edited by: Kurobei ]
I was planning on sticking with Al and have just learnt that putting a wooden core in your staff stops it from bending...........which is exactly why Im making a new one!!!
Does anyone have any suggestions as to what would be the best kind of wood to use for a core? It needs to have some flex but be quite strong.
Also, any info on fixing wicks would be appreciated, Im using double wicks.
Kuro
[ 21 August 2002, 20:36: Message edited by: Kurobei ]
whats up with all the limitations?
Delete TopicPosted:i can also attest to the smooth and lovely amazingness of ado-p's new staff.
he's making me one
hell, i even learned staff this weekend :wigglingdoobopingsmiley:
he's making me one
hell, i even learned staff this weekend :wigglingdoobopingsmiley:
My mind not only wanders, it sometimes leaves completely 
Posted:Right that's enough. When are you coming up to edinburgh ado-p?
Well?
Well?
"the now legendary" - Kaskade
"the still legendary" - Kaskade
I spunked in my friend's aquarium and the fish ate it. I love all fish. Especially the pink ones. They are my bitches. - Anon.
Posted:Will have pictures soon
The university of cork juggling soc has asked me to make a few sticks for them. i'll take piccies of some of them at different stages of construction.
stay tuned, same bat time, same bat channel.
*runs off to staff forum to post about contact bliss*
/edit for mcp
Hows January?
ps please pm me your poast addy, coz i lost it
EDITED_BY: ado-p (1099388401)
The university of cork juggling soc has asked me to make a few sticks for them. i'll take piccies of some of them at different stages of construction.
stay tuned, same bat time, same bat channel.
*runs off to staff forum to post about contact bliss*
/edit for mcp
Hows January?
ps please pm me your poast addy, coz i lost it
EDITED_BY: ado-p (1099388401)
Love is the law.
DeletePosted:tut tut tut...
January is okay, NOW is better...
January is okay, NOW is better...
"the now legendary" - Kaskade
"the still legendary" - Kaskade
I spunked in my friend's aquarium and the fish ate it. I love all fish. Especially the pink ones. They are my bitches. - Anon.
Posted:Written by: ado-p
The actual question is about the Ali istelf and the quality of it.
The Spec is: AI Mg Si 0,5. F22. Yeild Strentgh 215. Brinnel Hardness 70.
I dont really know what any of that stuff means. Can anybody explain it to me?
Turns out this kind of Ali bends when dropped really hard. Or do they all.
Im sure i read in a thread that you could get a spec the wouldnt bend so easy. Extruded?
Its possible that i could get annodised (sp?) but thats bound to be a bit more expensive than what im paying.
So made another one today but this time i put the dowel all the way through. Damn its heavy.
Seems to help with the contact though.
The weight seems to help me drop is less though. If that makes any sense
EDITED_BY: ado-p (1100025077)
The actual question is about the Ali istelf and the quality of it.
The Spec is: AI Mg Si 0,5. F22. Yeild Strentgh 215. Brinnel Hardness 70.
I dont really know what any of that stuff means. Can anybody explain it to me?
Turns out this kind of Ali bends when dropped really hard. Or do they all.
Im sure i read in a thread that you could get a spec the wouldnt bend so easy. Extruded?
Its possible that i could get annodised (sp?) but thats bound to be a bit more expensive than what im paying.
So made another one today but this time i put the dowel all the way through. Damn its heavy.
Seems to help with the contact though.
The weight seems to help me drop is less though. If that makes any sense
EDITED_BY: ado-p (1100025077)
Love is the law.
DeletePosted:
I manufacture all of my staffs from extruded 1.5 or 2 mm marine grade duralimin, I've never had one bend on me yet, considering the abuse that teaching myself staff has inflicted, just in the process of putting together an 11 foot quad burner, thats right, eight wicks, for use on my four foot stilts, thats going to have something like 16 foot of four inch kevlar. Typically though i make five to eight foot staffs, using 1.5mm, good solid weight etc,
mark
I manufacture all of my staffs from extruded 1.5 or 2 mm marine grade duralimin, I've never had one bend on me yet, considering the abuse that teaching myself staff has inflicted, just in the process of putting together an 11 foot quad burner, thats right, eight wicks, for use on my four foot stilts, thats going to have something like 16 foot of four inch kevlar. Typically though i make five to eight foot staffs, using 1.5mm, good solid weight etc,
mark
Delete
Similar Topics
Using the keywords [staff construction] we found the following similar topics.1. Learn > Dragon Staff > Mr Moustachios Monks Spade QR Guide > Staff Mode - Intro - QR *help/resource
2. Learn > 3 Section Staff (Sanjiegun) > Beginner > Staff Specs(Which staff should I get?) *help/resource
3. Learn > Dragon Staff > Mr. Moustachios Dragon Staff QR Guide > Chi - Forward-Anti Side to Side - QR *help/resource
4. Forums > Staff Contact Moves Book. Non-Definitive. - updated 10/06/06 [39 replies]
5. Learn > How to make your own gear > How to make your own pendulum poi > The construction *help/resource
Show more..
© 1998 - 2017 Home of Poi Ltd,
New Zealand unless otherwise stated.
All rights reserved
*All prices converted to United States dollars using XE.com.